Flexible type AE-400 series

The inquiry about this product

Features

  • Reduces stress under curing because it converts into a rubber-like flexible material when undergoes curing, and has flexibility enabling it to absorb mechanical impact, vibration and the like
  • Effective in bonding different types of materials between which there is a big difference in coefficient of thermal expansion, and has high bonding strength against peeling
  • AE-403H, AE-421D and AE-421H meet Br and Cl requirements for halogen free as defined in IEC 61249-2-21.
    (IEC 61249-2-1 definition:900 ppm maximum chlorine, 900 ppm maximum bromine, 1500 ppm maximum total halogens)
ページ上部へ戻る

Uses

  • Bonding parts which will be subjected to impact load, vibration load or the like
  • Bonding different kinds of materials
  • Bonding parts that are required to have flexibility
  • Bonding thin-film components in places where curling is undesirable
ITEM AE-40 AE-400 AE-403H AE-421D AE-421H Conditions
Features High
elongation
Good
adhesion
of plastics
Low-
halogen
contained,
Flowable
Low-
halogen
contained,
Low
bleed-out
Low-
halogen
contained,
High
thixotropy
-
Properties
before
curing
Appearance Pale
yellow
viscous
liquid
Black
viscous
liquid
Black
viscous
liquid
Black
viscous
liquid
Black
viscous
liquid
Visual
observation
Viscosity 50Pa・s 10Pa・s 6Pa・s 10Pa・s 16Pa・s E-type viscometer,
25degC, 20rpm
Thixotropic index 2.7 1.3 1.1 1.7 2.9 E-type viscometer,
25degC, 2rpm/20rpm
Recommended
cure schedule
60min at
120degC
30min at
80degC
30min at
80degC
30min at
80degC
30min at
80degC
Convection oven
heating
Properties
after
curing
Lap shear
strength
8N/mm2 14N/mm2 14N/mm2 17N/mm2 17N/mm2 JIS K-6850
(steel plate)
T-peel strength 38N
/25mm
32N
/25mm
20N
/25mm
90N
/25mm
90N
/25mm
JIS-K6854-3
(steel plate)
Glass transition
temperature
30degC 16degC 28degC 26degC 24degC TMA
Flexural
modulus
0.17GPa 0.27GPa - - - DMS,25degC
Young’s
modulus
10MPa 8MPa 50MPa 120MPa 150MPa JIS K-7161
Elongation at
break
250% 110% 140% 120% 90%
Water
absorption
1.5% 1.6% 2.5% 2.5% 1.6% 1h boiling

Technical data presented in this document are typical experimental values and do not signify any of the products’ specifications. The data may be revised without prior notice.